International Journal of Mechanical and Production Engineering (IJMPE)
.
Follow Us On :
current issues
Volume-9,Issue-1  ( Jan, 2021 )
Past issues
  1. Volume-8,Issue-12  ( Dec, 2020 )
  2. Volume-8,Issue-11  ( Nov, 2020 )
  3. Volume-8,Issue-10  ( Oct, 2020 )
  4. Volume-8,Issue-9  ( Sep, 2020 )
  5. Volume-8,Issue-8  ( Aug, 2020 )
  6. Volume-8,Issue-7  ( Jul, 2020 )
  7. Volume-8,Issue-6  ( Jun, 2020 )
  8. Volume-8,Issue-5  ( May, 2020 )
  9. Volume-8,Issue-4  ( Apr, 2020 )
  10. Volume-8,Issue-3  ( Mar, 2020 )

Statistics report
Apr. 2021
Submitted Papers : 80
Accepted Papers : 10
Rejected Papers : 70
Acc. Perc : 12%
Issue Published : 94
Paper Published : 2094
No. of Authors : 5972
  Journal Paper


Paper Title :
Comparison Of Tensile Strength And Water Absorption Properties Of Pva /Sago Starch And Pva/ Sago Starch Acetate

Author :Fatin Afiqah Juhari, Rahmah Mohamad, Nur Safwah Basri

Article Citation :Fatin Afiqah Juhari ,Rahmah Mohamad ,Nur Safwah Basri , (2015 ) " Comparison Of Tensile Strength And Water Absorption Properties Of Pva /Sago Starch And Pva/ Sago Starch Acetate " , International Journal of Mechanical and Production Engineering (IJMPE) , pp. 56-60, Volume-3,Issue-10

Abstract : Biodegradable plastic utilizing sago starch blended with PVA are fabricated and characterized in this study. PVA/sago starch and PVA/sago starch acetate system was prepared via casting method and starch acetate having degree of substitution (DS) 0.30 was prepared by acetylation process. The different percentage ratios of 50 to 90% of sago starch (SS) and sago starch acetate (SSA) for PVA blends were hot solution casted and mechanical properties, water absorption properties and transition temperature blends were observed. From water absorption analysis up to 10days, weight gains were observed for all blends as they are hydrophilic and highly absorb water. All samples showed rapid increase in weight gain at initial hydration. Higher water absorption were obtained with PVA/SSA as compared to PVA/ SS with percent water absorption between 35 to 60% for PVA/SS and 15 to 44% at room temperature. PVA/SSA blend had increased the hydrophobicity of starch and reduces swelling power of film. From DSC thermogram performed, the highest gelatinization temperature were obtained by the composition of 20% PVA / 80% SS of 241ºC. PVA/SSA with 50%PVA/50%SA ratios had gelatinization temperature of 208 ºC. The difference in gelatinization temperature indicated differences in the perfection of starch crystals. The higher the gelatinization temperature, crystals are more perfect in the crystal lattice. Generally, PVA/SSA blend have higher Tensile strength compared to PVA/SS for all preparations. Higher SSA content also increases the modulus and improved rigidity. Microscopy images also showed better dispersion and homogeneity of PVA/SSA compared to PVA/SS. Hence PVA/SSA using modified sago starch has improved mechanical and better resistant to water. Index Terms- Polyvinyl alcohol, Sago starch, Sago starch acetate, Tensile, Water absorption.

Type : Research paper

Published : Volume-3,Issue-10


DOIONLINE NO - IJMPE-IRAJ-DOIONLNE-3022   View Here

Copyright: © Institute of Research and Journals

| PDF |
Viewed - 82
| Published on 2015-10-09
   
   
IRAJ Other Journals
IJMPE updates
We are happy to announce that Dr. R. A. SAVANUR joined as the CHief Editor for IJMPE.
The Conference World

JOURNAL SUPPORTED BY