Paper Title :Damage Behaviors Of Glass Fabric Honeycomb Sandwich Composite Materials Under Static Loading
Author :Ramadan Mohmmed, Azzam Ahmed, Mohamed Ahmed Elgalib, Akram H M Ali, Hasabo A.Mhd Ahmed
Article Citation :Ramadan Mohmmed ,Azzam Ahmed ,Mohamed Ahmed Elgalib ,Akram H M Ali ,Hasabo A.Mhd Ahmed ,
(2016 ) " Damage Behaviors Of Glass Fabric Honeycomb Sandwich Composite Materials Under Static Loading " ,
International Journal of Mechanical and Production Engineering (IJMPE) ,
pp. 35-40,
Volume-4,Issue-5
Abstract : Sandwich Composite structures have been widely used in the fields of aircrafts. Investigations of the mechanical
properties of sandwich composite structures play a vital role in deciding their applicability in various engineering fields. The
objectives of this work are fabricating the sandwich composite structures with honeycomb/woven glass fabric using Vacuum
Assisted Resin Transfer Molding. In order to evaluate the internal and external damage resulting under (three point bending,
compression, tensile loading) tests using product computerized universal testing machine. The load-displacement curves
were obtained to characterize the failure mechanisms of sandwich composite structures. The failure modes were studied, it
was observed that in the start matrix crack after that delimitation between two layers, finally the final failure occurred when
the face sheet failure.
Keywords- Sandwich Composite, Honeycomb/Woven Glass fabric, Static tests, Failure Modes.
Type : Research paper
Published : Volume-4,Issue-5
DOIONLINE NO - IJMPE-IRAJ-DOIONLINE-4601
View Here
Copyright: © Institute of Research and Journals
|
|
| |
|
PDF |
| |
Viewed - 81 |
| |
Published on 2016-06-08 |
|