Paper Title :Metal Hydride Formation By Mg Alloy Sintered Powder For Hydrogen Storage Application
Author :Ken Ninez, Muhammad Junaidi, Haryati Purwaningsih
Article Citation :Ken Ninez ,Muhammad Junaidi ,Haryati Purwaningsih ,
(2014 ) " Metal Hydride Formation By Mg Alloy Sintered Powder For Hydrogen Storage Application " ,
International Journal of Mechanical and Production Engineering (IJMPE) ,
pp. 26-28,
Volume-2,Issue-1
Abstract : Abstract— Hydrogen storage is clearly one of the key challenges in developing hydrogen economy [2]. Magnesium based
alloys can be used for Hydrogen Storage Materials. The composition of Mg-Al alloy is Mg-42 at.% Al and synthesized by
40hours milling time to produced MgAl solid solution. Powder from milling process sintered temperature 600o
C and two
hours holding time at argon environment to produced Mg17Al12 phase.
Mg17Al12 powder hydrogenated at 1 MPa pressure and the temperature is 4000
C with variation time 1, 2 , dan 3 hour. XRD
analysis identified the MgH2 phase, and the result is 1.242%, 3.082% and 4.2% after hydriding time 1, 2, 3 hours.
Type : Research paper
Published : Volume-2,Issue-1
DOIONLINE NO - IJMPE-IRAJ-DOIONLINE-472
View Here
Copyright: © Institute of Research and Journals
| |
 |
| |
 |
PDF |
| |
Viewed - 45 |
| |
Published on 2014-02-18 |
|