International Journal of Mechanical and Production Engineering (IJMPE)
.
Follow Us On :
current issues
Volume-9,Issue-1  ( Jan, 2021 )
Past issues
  1. Volume-8,Issue-12  ( Dec, 2020 )
  2. Volume-8,Issue-11  ( Nov, 2020 )
  3. Volume-8,Issue-10  ( Oct, 2020 )
  4. Volume-8,Issue-9  ( Sep, 2020 )
  5. Volume-8,Issue-8  ( Aug, 2020 )
  6. Volume-8,Issue-7  ( Jul, 2020 )
  7. Volume-8,Issue-6  ( Jun, 2020 )
  8. Volume-8,Issue-5  ( May, 2020 )
  9. Volume-8,Issue-4  ( Apr, 2020 )
  10. Volume-8,Issue-3  ( Mar, 2020 )

Statistics report
Apr. 2021
Submitted Papers : 80
Accepted Papers : 10
Rejected Papers : 70
Acc. Perc : 12%
Issue Published : 94
Paper Published : 2094
No. of Authors : 5972
  Journal Paper


Paper Title :
Effect of High Power Ultrasonic Irradiation to the Magnetic Properties of Bafe12o19/Cofe2o4 Composite

Author :Gemi Nastiti, Azwar Manaf

Article Citation :Gemi Nastiti ,Azwar Manaf , (2017 ) " Effect of High Power Ultrasonic Irradiation to the Magnetic Properties of Bafe12o19/Cofe2o4 Composite " , International Journal of Mechanical and Production Engineering (IJMPE) , pp. 132-135, Volume-5,Issue-2

Abstract : Magnetic properties of composite magnets made of Barium Hexaferrite (BHF) and CoFe 2 O 4 were reported in this paper. Effect of variation ultrasonic irradiation caused to the magnetic properties of the composite. The two types of magnetic particles have a high total magnetization value which was required for permanent magnet applications. Both CoFe 2 O 4 and BHF were synthesized through mechanical alloying coupled with high frequency ultrasonic irradiation. In this respect, mechanically milled BHF precursors was sintered at a temperature of 1250 0 C for 2 hours leading to single phase powders. A similar method was also employed in the preparation of CoFe 2 O 4 materials, but this required a relatively longer sintering time up to 12 hours at a sintering temperature of 900 0 C. Composite magnets were obtained after sintering the mechanically mixed the two types as constituted components of the composite. The enhancement in remanent magnetization raised aboutthe effect of grain exchange interaction between hard and soft magnetic phases.The results studied by XRD, Permagraph and SEMrespectively. Index terms- BaFe 12 O 19 , CoFe 2 O 4 , Composite, Permanent magnet.

Type : Research paper

Published : Volume-5,Issue-2


DOIONLINE NO - IJMPE-IRAJ-DOIONLNE-7026   View Here

Copyright: © Institute of Research and Journals

| PDF |
Viewed - 51
| Published on 2017-04-20
   
   
IRAJ Other Journals
IJMPE updates
We are happy to announce that Dr. R. A. SAVANUR joined as the CHief Editor for IJMPE.
The Conference World

JOURNAL SUPPORTED BY